Abstract: In order to improve the electrochemical performance of the neural electrode the polyaniline coatings were modified on roughened Pt (PANI/rPt1) electrodes using electrochemical method. The roughness factor (fR up to 424) of Pt surfaces increased significantly through electrochemical roughening processing. PANI/rPt electrodes showed excellent interfacial properties. Specifically, about 5.6-fold increase in the charge density of PANI/rPt (fR = 424) was observed, while the interfacial impedance (103.5 Ω) was reduced by 50% compared to that of PANI coatings on the smooth Pt surfaces (PANI/sPt2). The results indicate the potential application of PANI/rPt as an efficient and stable future neural interface. In addition, the wear test shows that the coating did not fail during the wearing period and holds an excellent wear resistance ability.