Authors: Endo, M.M. | Barbour, P.S.M. | Barton, D.C. | Fisher, J.; | Tipper, J.L. | Ingham, E. | Stone, M.H.
Affiliations: School of Mechanical Engineering, University of Leeds, Leeds, LS2 9JT, UK | Department of Microbiology, University of Leeds, Leeds, UK | Department of Orthopaedic Surgery, Leeds General Infirmary, Leeds, UK
Note: [] Corresponding author.
Abstract: The wear debris generated from ultra high molecular weight polyethylene (UHMWPE) have been recognised as one of the major causes of failure in total hip replacements (THR). It is essential to reduce the wear debris generated from UHMWPE acetabular cups in order to minimise this problem. Debris in the submicron size range is believed to have greater osteolytic potential [1]. It is now known that crosslinked UHMWPE acetabular cups have reduced volumetric wear rates but little is known about the influence of crosslinking on the size and morphology of the wear debris. In this study, the wear of grade GUR 1020 crosslinked (vacuum gamma irradiated), GUR 1120 crosslinked (acetylene enhanced irradiated) and non cross linked (ethylene oxide sterilised) GUR 1020 UHMWPE was compared in multidirectional pin‐on‐plate wear tests under three different counterface conditions (smooth, isotropically rough and scratched counterfaces). Multidirectional motion was chosen because this motion was closer to the relative motion in the natural hip. From this study, better wear resistance of crosslinked UHMWPE compared with non‐crosslinked UHMWPE was demonstrated for the smooth counterface conditions. However, in the rough and scratched counterface conditions, the vacuum gamma irradiated crosslinked material produced significantly higher wear rates than the non‐crosslinked material. The analysis of the wear debris showed that the majority of the volume of the acetylene enhanced crosslinked UHMWPE wear debris was in the most biologically active size range (0.1 to 0.5 μm). In contrast, the non‐crosslinked material and the vacuum gamma irradiated crosslinked material had a greater proportion of the volume of the debris in the larger size ranges which are less biologically active. This has important implications for its osteolytic potential.
Journal: Bio-Medical Materials and Engineering, vol. 11, no. 1, pp. 23-35, 2001
IOS Press, Inc.
6751 Tepper Drive
Clifton, VA 20124
USA
Tel: +1 703 830 6300
Fax: +1 703 830 2300
sales@iospress.com
For editorial issues, like the status of your submitted paper or proposals, write to editorial@iospress.nl
IOS Press
Nieuwe Hemweg 6B
1013 BG Amsterdam
The Netherlands
Tel: +31 20 688 3355
Fax: +31 20 687 0091
info@iospress.nl
For editorial issues, permissions, book requests, submissions and proceedings, contact the Amsterdam office info@iospress.nl
Inspirees International (China Office)
Ciyunsi Beili 207(CapitaLand), Bld 1, 7-901
100025, Beijing
China
Free service line: 400 661 8717
Fax: +86 10 8446 7947
china@iospress.cn
For editorial issues, like the status of your submitted paper or proposals, write to editorial@iospress.nl
如果您在出版方面需要帮助或有任何建, 件至: editorial@iospress.nl